CERA MEDICAL
MaterialsZirconia BlanksMetal & Metal-Free MaterialsFinishing & Consumables

Products in this section

PRITIDENTA · UPCERA

HT White
UPCERA

HT White

Maximum-strength substructures and everyday zirconia

Learn more
ST Pre-shaded
UPCERA

ST Pre-shaded

Reliable, versatile everyday zirconia

Learn more
Explore Functional
UPCERA

Explore Functional

Our most popular zirconia — balanced for a wide range of indications

Learn more
Multi Translucent PLUS (MTP)
PRITIDENTA

Multi Translucent PLUS (MTP)

For the highest standards — Made in Germany

Learn more
DUO Multilayer
UPCERA

DUO Multilayer

Strength, aesthetics, efficiency and versatility in one disc

Learn more
HT White

HT White — 3-unit posterior bridge

HT White discs
UPCERA · Zirconia Family

HT White

Maximum-strength substructures and everyday zirconia

CE 0197FDAOpen CAD/CAM

A high-strength 3Y-TZP zirconia for monolithic or anatomically-reduced anterior restorations and framework bridges.

1300MPaFlexural Strength
39%Translucency
10–25mmDisc Thickness
3YTZPRaw Material
Indications
  • Copings & frameworks
  • Substructures
  • Posterior bridges
  • Anatomically-reduced anterior restorations
Technical specification
Raw material3Y-TZP (yttria-stabilised tetragonal zirconia polycrystal)
Flexural strength1300 MPa
Translucency39%
Disc thickness10, 12, 14, 16, 18, 20, 25 mm
ShadeWhite (dyeing-liquid compatible)
SystemOpen CAD/CAM system
CertificationsCE 0197 · FDA
Request a quoteEmail us
ST Pre-shaded

ST Pre-shaded (ST-Color) discs

UPCERA · Zirconia Family

ST Pre-shaded

Reliable, versatile everyday zirconia

Pre-shadedAnti-agingOpen CAD/CAM

Pre-shaded 3Y-TZP with optimal stability and outstanding anti-aging performance across eleven shades.

1300MPaFlexural Strength
43%Translucency
3YTZPRaw Material
11shadesPre-shaded
Indications
  • Single crowns
  • Multi-unit frameworks
  • Posterior restorations
  • Copings
Available shades
A1A2A3A3.5A4C2D2D3OM1OM2OM3
Technical specification
Raw material3Y-TZP
Flexural strength1300 MPa
Translucency43%
ShadesA1 · A2 · A3 · A3.5 · A4 · C2 · D2 · D3 · OM1 · OM2 · OM3
Anti-agingOptimal stability, outstanding anti-aging performance
SystemOpen CAD/CAM system
Recommended sintering programme
04008001200160001002003004005006001530°C · hold 120 minTemperature / °CTime / min
1530°CPeak
120 minHold
8°C/minTypical ramp

Total cycle approx. 11 hours including natural cooling. Always refer to the manufacturer's instructions for use.

Request a quoteEmail us
Explore Functional

Explore Functional A2 · D98-16

UPCERA · Zirconia Family

Explore Functional

Our most popular zirconia — balanced for a wide range of indications

Best sellerMultilayerCerec compatible

A seamless balance of chroma, translucency and strength — the one disc most laboratories reach for first.

1027–1300MPaFlexural Strength
43–46.6%Translucency
4Y/5YPSZRaw Material
20shadesShade Range
Indications
  • Full-contour anterior crowns
  • Posterior crowns
  • Multi-unit bridges
  • Inlays & onlays
  • Veneers
Available shades
A1A2A3A3.5A4B1B2B3B4C1C2C3C4D2D3D4BL1BL2BL3BL4
Technical specification
Raw material4Y/5Y-PSZ, multilayer gradient
Flexural strength1027–1300 MPa (layer dependent)
Translucency43–46.6%
Shades16 VITA classical + BL1–BL4
SystemOpen CAD/CAM · compatible with Cerec in-lab (Sirona)
Recommended sintering programme
04008001200160001002003004005006001480°C · hold 120 minTemperature / °CTime / min
1480°CPeak
120 minHold
8°C/minTypical ramp

8°C/min ramp · 30 min hold at 1150°C · natural cooling below 800°C. Always refer to the manufacturer's instructions for use.

Request a quoteEmail us
Multi Translucent PLUS (MTP)

MTP 7-unit bridge, finished with priti®perfect, shade A2

PRITIDENTA · Made in Germany
PRITIDENTA · priti®multidisc ZrO₂

Multi Translucent PLUS (MTP)

For the highest standards — Made in Germany

Made in GermanyUp to 14 unitsCut-back

Higher translucency and finer layering than standard Multi Translucent — PRITIDENTA's "one-for-all" material.

≥1150MPaFlexural Strength
45–49%Translucency
14unitsMax Span
19shadesShade Range
Indications
  • Single crowns, inlays, onlays, veneers
  • Bridges up to 14 units
  • Implant-supported superstructures up to 14 units
  • Cut-back technique
Available shades
All 16 VITA classical shades3 bleach shades
Technical specification
Raw material4Y/5Y-TZP, graded multilayer
Flexural strength≥1150 MPa
Translucency45–49%
Disc heights14, 16, 18, 20, 25 mm
ShadesAll 16 VITA classical + 3 bleach
OriginMade in Germany
LimitationsNone
Recommended sintering programme
04008001200160001002003004001450°C · hold 120 minTemperature / °CTime / min
1450°CPeak
120 minHold
8°C/minTypical ramp

Standard programme — 7 hours total cycle. Ramp and cool 8–10°C/min. Always refer to the manufacturer's instructions for use.

Request a quoteEmail us
DUO Multilayer

DUO Multilayer A2 · D98-14

UPCERA · Zirconia Family

DUO Multilayer

Strength, aesthetics, efficiency and versatility in one disc

UPD technologyCE 0197FDA

Built on UPCERA's Uniform Particle Dispersion (UPD) technology for consistent sintering with reduced deformation.

850–1200MPaFlexural Strength
45–48%Translucency
4Y/5YPSZRaw Material
12–30mmDisc Thickness
Indications
  • Fully anatomical anterior & posterior crowns
  • Multi-unit bridges
  • Implant-supported restorations
  • Inlays, onlays and veneers
Available shades
A1A2A3A3.5A4B1B2B3C1C2C3D2D3D4BL1BL2BL3BL4
Technical specification
Raw material4Y/5Y-PSZ multilayer
Flexural strength850–1200 MPa
Translucency45–48%
Disc thickness12–30 mm
TechnologyUniform Particle Dispersion (UPD)
CertificationsCE 0197 · FDA
Recommended sintering programme
04008001200160001002003004005006001480°C · hold 120 minTemperature / °CTime / min
1480°CPeak
120 minHold
8°C/minTypical ramp

8°C/min ramp · 30 min hold at 1150°C · natural cooling below 800°C. Always refer to the manufacturer's instructions for use.

Request a quoteEmail us